  • ABS Resin 1000

ABS Resin 1000

Production country: Taiwan

Cost in place: Moscow

Выберите город:

Цена по запросу

Min. order qty 17 t

Основные характеристики

  • Brand

    TAITALAC®

  • Grade

    High impact grade

  • Processing method

    Extrusion, Injection Molding

  • Tensile Strength at Yield

    40 MPa

  • Tensile Strength at Break

    35 MPa

  • Elongation at Break

    30 %

  • Melt flow index

    16 g/10min

  • Rockwell Hardness

    110 R-scale

Similar goods

Описание:

ABS is the terpolymer of Acrylonitrile-Butadiene-Styrene. Each of the three components possesses certain functions. Acrylonitrile provides chemical resistance and hardness, Butadiene contributes toughness and impact strength; Styrene offers gloss and process-ability. Combining the above characteristics, ABS is now the most popular and economical Engineering Plastic.

TAITALAC®is the trade name of TTC’s ABS resin. Adopting the famous Japanese Toray Process, TAITALAC® is enjoying a reputation for excellent quality and recognized as one of the leading ABS / SAN resins in the world.

ABS Resin TAITALAC® 1000 description:

  • Extrusion/Injection
  • High impact 
  • Good flow for process 
  • High gloss 
  • An optimum balance of physical properties with high impact and good flow

APPLICATION 

  • Computer / TV / telephone housing 
  • Toy and furniture components 
  • Extrusion film 
  • Office equipment 
  • Kitchen appliances 
  • House-ware 
  • Battery 
  • Shoes

General properties

  • Grade: High impact grade
  • Processing method: Extrusion, Injection Molding
  • Application: Computer/ TV/ telephone housing , Furniture components , Kitchen appliances , House-ware , Battery and parts, Shoes and parts

Thermal properties

  • Test Condition:: 220℃, 10kg load
  • Melt flow index: 16 g/10min
  • Heat Distortion Temperature : 84 °C
  • Vicat Softening Temperature : 97 °C

Mechanical properties

  • Test Condition: : 23℃, 1/8 inch, 5 mm/min
  • Tensile Strength at Yield: 40 MPa
  • Tensile Strength at Break : 35 MPa
  • Elongation at Break : 30 %
  • Flexural yield strength: 70 MPa
  • Flexural Modulus : 2400 MPa

Physical properties

  • Rockwell Hardness : 110 R-scale
  • Mold Shrinkage: 0.4 %
  • Water Absorption : 0.3 %
  • Izod Impact Strength: 25 kg-cm/cm
  • Test Condition : 23℃, 1/8" notched