SAN-resin PN-127H
  • SAN-resin PN-127H

SAN-resin PN-127H

Production country: Taiwan

Cost in place: Moscow

Выберите город:

Цена по запросу

Min. order qty 17 t

Основные характеристики

  • Brand

    KIBISAN®

  • Grade

    High chemical resistant

  • Processing method

    Injection Molding

  • Tensile Strength at Yield

    79 MPa

  • Melt flow index

    18 g/10min

Similar goods

Описание:

SAN is a copolymerization of styrene-acrylonitrile. Acrylonitrile monomer (AN) is added to styrene monomer (SM) to copolymerize SAN, also commonly known as the AS Resin. SAN not only retains the transparency of GPPS, it also has more chemical resistance and slightly increased surface hardness. Under natural conditions, it is a bright yellowish transparent object.

Application:

Toothbrush handles / battery casings / lighter casings / any transparent molded products requiring high strength

General properties

  • Grade: High chemical resistant
  • Processing method: Injection Molding
  • Application: General chemical resistance products, Lighters casings, Battery casings, Toothbrush handles, High strengt transparent products

Thermal properties

  • Test Condition:: 220℃, 10kg load MPa
  • Melt flow index: 18 g/10min
  • Heat Distortion Temperature : 91 °
  • Vicat Softening Temperature : 107 °

Mechanical properties

  • Test Condition: : 23℃, 1/8 inch, 5 mm/min
  • Tensile Strength at Yield: 79 MPa
  • Tensile Strength at Break : 79 MPa
  • Elongation at Break : 7 %
  • Flexural yield strength: 109 MPa
  • Flexural Modulus : 3600 MPa

Physical properties

  • Mold Shrinkage: 0.5 %
  • Izod Impact Strength: 1.9 kg-cm/cm
  • Test Condition : 23℃, 1/8" notched