SAN-resin PN-137H
  • SAN-resin PN-137H

SAN-resin PN-137H

Production country: Taiwan

Cost in place: Moscow

Выберите город:

Цена по запросу

Min. order qty 17 t

Основные характеристики

  • Brand

    KIBISAN®

  • Grade

    High chemical resistant

  • Processing method

    Injection Molding

  • Tensile Strength at Yield

    83 MPa

  • Melt flow index

    12 g/10min

Similar goods

Описание:

SAN is a copolymerization of styrene-acrylonitrile. Acrylonitrile monomer (AN) is added to styrene monomer (SM) to copolymerize SAN, also commonly known as the AS Resin. SAN not only retains the transparency of GPPS, it also has more chemical resistance and slightly increased surface hardness. Under natural conditions, it is a bright yellowish transparent object.

Application:

Lighters / high chemical resistance molded product

General properties

  • Grade: High chemical resistant
  • Processing method: Injection Molding
  • Application: General chemical resistance products, Lighters casings, High strengt transparent products

Thermal properties

  • Test Condition:: 220℃, 10kg load MPa
  • Melt flow index: 12 g/10min
  • Heat Distortion Temperature : 91 °
  • Vicat Softening Temperature : 105 °

Mechanical properties

  • Test Condition: : 23℃, 1/8 inch, 5 mm/min
  • Tensile Strength at Yield: 83 MPa
  • Tensile Strength at Break : 83 MPa
  • Elongation at Break : 7 %
  • Flexural yield strength: 123 MPa
  • Flexural Modulus : 4000 MPa

Physical properties

  • Mold Shrinkage: 0.5 %
  • Izod Impact Strength: 2.3 kg-cm/cm
  • Test Condition : 23℃, 1/8" notched